Structure and Mechanical and Technological Properties of Additive Material for Welding Heat-Resistant Steels
DOI:
https://doi.org/10.20998/2078-774X.2019.01.07Анотація
The analysis of casting defects in the hull parts of power equipment, and their elimination methods. The development directions of foreign researchers in the field of heat-resistant steels welding are established and analyzed. The prospects of using pearlite material for electric arc welding of defects is shown. The results of studies of the welding material of a pearlite structure, microalloyed by rare-earth metals, with high welding-technological, viscoplastic properties and impact strength are presented. An analysis of the state of scientific developments of metallurgists, material scientists and welders shows that, to ensure high viscoplastic properties of steel products, a promising direction is the use of rare earth metals as modifiers and microalloying additives as desulfurizers. The welding process is carried out without heating and subsequent heat treatment. For research, an experimental batch of electrodes was manufactured as rods in which the wire SV-08A was used. Doping was provided through an electrode coating. Alloying with rare-earth metals was carried out by introducing yttrium ligature into the coating, it was found that the introduction of rare-earth metals into the deposited metal allows to obtain high visco-plastic properties of the metal without reducing the carbon content, which, in turn, provides strength properties at the level specified by regulatory documentation.
Посилання
Panov V. I. (2007), “Universal'naja metodika remontnoj svarki krupnogabaritnyh massivnyh konstrukcij tjazhelogo mashinostroenija [A universal technique for repair welding of large-sized massive structures of heavy engineering]”, Svarochnoe proizvodstvo [Welding production], pp. 11–17.
Nazarchuk A. T. Snisar V. V., Demchenko E. L. (2003), “Poluchenie ravnoprochnyh svarnyh soedinenij zakalivayushihsya stalej bez podogreva i termicheskoj obrabotki [Obtaining equal strength welded joints of hardened steels without heating and heat treatment]”, Avtomat. svarka [Automatic Welding]. no. 5,. pp. 41–46.
(1978), Cobe steel welding consumabels, Catalog-Tokyo [Catalog-Tokyo], 103 p.
Anahov A. E. Korolkov P. M. (2003), Svarka i termicheskaya obrabotka korpusnogo energeticheskogo oborudovaniya pri remonte [Welding and heat treatment of case power equipment during repair.], Ekotehnologiya [Ecotechnology], Kiev, 87 p.
Iositecu N. (1971), Newer. Metal, Ind. vol. 16, no. 5. pp. 107–110.
Efimenko N. G. (2017), Redkozemelnye metally v svarochnyh materialah [Rare earth metals in welding consumables], PF. Collegium, Kharkiv, 187 p, ISBN 978-966-97418-9-9.
Rychkov A. P., Lanskaya K. A., Tyurin E. I. (1973), “Vliyanie RZM na strukturu i svojstva kotelnyh stalej 20K i 12H1MF [The influence of rare-earth metals on the structure and properties of boiler steels 20K and 12Kh1MF]”, Stal [Steal], no. 10, pp. 930–932.
Nakao E., Nisimoto K. (1984), “Ohrupchivanie naplavlennogo metalla v svarnyh shvah vysokochistoj hromomolibdenovoj (19 Cr–2Mo) stali i ego umenshenie putem vvedeniya dobavok redkozemelnyh [Embrittlement of deposited metal in welds of high-purity chromium-molybdenum (19Cr – 2Mo) steel and its reduction by introducing rare-earth additives]”, Esecu gakaj rombunsyu [Yessetsu gakai rhombunshu], no. 2, pp. 325–331.